51CRV4 (50CRV4, AISI6150),material is chromium vanadium type spring steel normally supply cold rolled condition in coil or sheet, also it is able oil hardened and tempered process after that it will be with excellent wear resistance, toughness and shock good suitable to produce auto high stress parts.

High carbon steel strip for shoes insoles, shanks and toe caps.

C45E, C50S, C55S, C60S, C67S,C70S, C75S

Cold rolled and quenching high carbon steel strip

1 Good mechenical propeties and process perfomance

2. High harenability

3. Adding vanadium to refine the grain of steel

4. Reducing superheat sensitivity

5. Improving his strength and toughtness

6. High fatigue strength and yield ratio

Cold rolled 51crv4 spring steel strip coil for auto parts clutch disc and plates.

Production of width  from 4mm to 1200MM.

Thickness 0.15 up to 10mm

Grade with SAE1055,SAE1060,SAE1065,SAE1070,SAE1075,SAE1080,

SAE1095,51CRV4,60SI2MN.ETC

Thickness: 0.15mm---3.0mm

Width : 6mm---600mm

Tensile strength : 545-585mpa

Yield strength: 390-490mpa

Elongation:  10-29%

Hardness: 88-92hrc

Coil ID:300MM,400MM, 500MM

Grade with SAE1055,SAE1060,SAE1065,SAE1070,SAE1075,SAE1080,

SAE1095,51CRV4,60SI2MN.ETC

Thickness: 0.15mm---3.0mm

Width : 6mm---600mm

Tensile strength : 545-585mpa

Yield strength: 390-490mpa

Elongation:  10-29%

Hardness: 88-92hrc

Coil ID:300MM,400MM, 500MM